Tensile test on Strips and Plastic Films

ISO 527-3, ASTM D 882

ISO 527-3, ASTM D 882

ASTM D882 and ISO 527-3 are common standards that are used to determine the tensile properties of plastic film or sheets

This test allows to determine properties as tensile strength, yield strength, yield strain, strain at break, and modulus of elasticity. Due to the flexible, delicate nature of these plastic specimens, both gripping and strain measurement can be a challenge

Specimens are easily produced by a cutting press or a film cutting device. Dumbbell specimens are often used for quality control and require a direct measuring extensometer for strain acquisition directly on the specimen. For tests on strips the results for strain at break depend on the shape and the clamping type of the specimen. 25 mm x 25 mm rubber grip face size is commonly used for this material, that matches the width of the gripped or tabbed end of the specimen. The matching width allows for ease of specimen alignment, which is critical for good breaks and accurate test results. The gripping must prevent slipping of the material at relatively high loads but not tear into the material and cause premature specimen failure

We suggest to use parallel grips for applying enough pressure to avoid specimen slippage as premature failure and Video Extensometer to measure accurately strain values. The measuring principle is based on intelligent image analyses of two contrast marks on the specimen. The marks will be identified and the displacement will be evaluated as elongation depending on the gage length. Marking with paint pens and marking templates are provided with the instrument. Non-contacting video extensometry is usually the best solution, as typical clip-on extensometers weigh down the specimen, while knife edges tear at the specimen - both affecting test results

Our testing software has advanced pre-built methods available with pre-configured plastic specific calculations helping to ensure compliance. Using features such as an appropriate preload is critical for achieving accurate, repeatable results. A preload eliminates the compressive forces on a specimen that often occur when initially placed into grips

Are you interested in our machines and solutions? Contact Now


Questa prova di trazione secondo ISO 527 e ASTM D882 permette di determinare proprietà come stress di snervamento, deformazione di snervamento, sollecitazione massima e deformazione nominale a rottura
La natura flessibile e delicata di questi provini in plastica rende sia l’afferraggio quanto la misura della deformazione spesso difficili da gestire. L’afferraggio deve impedire sia lo scivolamento del materiale a carichi relativamente alti sia eventuali strappi, al fine di evitare premature rotture del provino. Le macchine di prova GALDABINI sono dotate di afferraggi adatti per condurre correttamente la prova di trazione su film plastico
L'estensimetro più indicato per tale prova è il Video Estensimetro (VideoXT), strumento di misura contactless che permette di misurare con precisione i valori di deformazione, semplicemente usando un pennarello base d'acqua per marcare la posizione dei lati sul materiale valutando così lo scivolamento di ciascun provino. La macchina di prova GALDABINI può essere facilmente equipaggiata con l’estensimetro VideoXT per una accurata misurazione della deformazione che avviene durante la prova di trazione su film plastico secondo ISO 527 e ASTM D882
Il nostro software GALDABINI Labtest dispone di metodi pre-costruiti avanzati con calcoli plastici specifici preconfigurati che contribuiscono a garantire la conformità. L'utilizzo di funzioni come un pre-carico adeguato è fondamentale per ottenere risultati precisi e ripetibili per condurre correttamente test di trazione su film plastico